gas flux cored welding wires

Produced in China, this welding wires benefits from a stable supply chain, rapid response to inquiries, localized technical support, manageable costs, and flexible delivery schedules to suit Screw conveyor, scraper, fan blades, pulverizer mill, fan grinding back powder, ash discharge pipe, maintenance and repair projects.
Product Description:

Single-layer hard surface surfacing, higher chromium carbide, composite carbide alloy wear resistant wires. 15-25Cr CO2 gas flux cored welding wires HRC60-65 anticorrosion for pulverizer mill/fan blades. 

Use: Screw conveyor, scraper, fan blades, pulverizer mill, fan grinding back powder, ash discharge pipe.

Deposited metal chemical composition (%) (Protective gas: CO2)

Chemical Composition(Guarantee Value)：

C 2.5-4.0

Mn -

Cr 15-25

B -

rest 8.0

Reference current ( DC+)

Welding voltage 26V

Diameter Φ1.2, Φ1.6, Φ1.4(mm) welding current all are 220(amps)

Key attributes:

diameter: 1.2mm 1.6mm 1.4mm

flux content: Standerd

material: flux cored welding wires

melting point: international standard

weight: 15kg 25kg 250kg 300kg

place of origin: Hebei, China

model number: d112

brand name: Naidi

application: pulverizer mill, fan grinding back

Product name: hard wearing resistant surfacing all kinds of welding wires d112

Packing: 15kg/plastic spool 25kg/coil 250kg 300kg/drum

Model: d112

Trade Term: FOB CIF

Advantage: anticorrosion,crack resisitance

Color: bright finish

OEM: Accept OEM

application: Screw conveyor, scraper,

hrc: 60-65

Protective gas: CO2

Packaging and delivery:

Selling Units: Single item

Single package size: 37X17X17 cm

Single gross weight: 15.000 kg

Precautions:

1. Welding work should be done degreasing, rust treatment.

2. Welding, the gas flow is generally 20 ~ 25L / min.

3. When the flux-cored wire is welded, the dry elongation should be 15 ~ 25mm.

4. Should be preheated to about 300 ℃ before welding large workpiece.

5. The humidity of the welding stock should be kept at less than 60%.