This MIG cobalt-based welding wires exhibits good corrosion resistance, heat resistance, and wear resistance up to 800 degrees Celsius. Suitable for high-temperature and high-pressure valves, chemical fiber cutting edges, and more. Available in diameters of 0.8mm-1.6mm with a composition of Co-Cr-W surfacing alloy. Supports OEM customization with a MOQ of 15kg.

aws ERcocr-b

ND-112 aws ERcocr-b In the continuous casting of cobalt based welding wires, carbon and tungsten content is higher, with moderate hardness, abrasion resistance than aws Ercocr-a good, but slightly less toughness. Surfacing layer has a good corrosion resistance, heat and wear resistance, to 800 degrees Celsius temperature can maintain these characteristics. Surfacing layer can be machined.

Uses: For high temperature and high pressure valves, internal combustion engine valves, chemical fiber cutting edge, high-pressure pump shaft sleeve and liner sleeve, wood saw tooth, hot rolling finishing roller pass

Key attributes:

diameter: 0.8-1.6mm-6.0mm

flux content: no

material: cobalt based welding wires

melting point: standard

customized support: OEM, ODM, OBM

weight: mig15kg tig 5kg

place of origin: Hebei, China

model number: aws a5.21 ercocr-e ercocr-a

brand name: hbndnm

application: high pressure valves, hot shear blade

Product name: aws a5.21 ercocr-e mig cobalt-based weliding wires 1.2mm factory

Material: cobalt based welding wires

Diameter: 0.8mm-1.6mm

Feature: good corrosion resistance

OEM: Accept

Composition: Co-Cr-W surfacing alloy

Package: 15kgs/spool/carton

Sample: Avaiable

cr: 26-32

MOQ: 15kg

Packaging and delivery：

Selling Units: Single item

Single package size: 38X20X20 cm

Single gross weight: 17.000 kg

Chemical composition of Welding wire (%):

c 1.2-1.7

cr 26-32

ni <=3.0

fe <=3.0

w 7.0-9.5

co bal.

Physical properties(as reference):

Proportion 8.47 kg/dm3

Melting temperature 1255-1341 ℃

specific heat 0.098 k/g. ℃        

coefficient of linear expansion 10-6/k(20-600℃) 14.1

Mechanical properties of deposited metal (as reference):

Tensile strength mpa: 840

Hrc under common temperature: 45-50

Hv under high temperature:

500℃ 380

600℃ 365

700℃ 348

800℃ 318